I-ductile intsimbi iqulathe i-iron, ikharbon, kunye nesilicon. Xa iarhente yokuqhekeza iyongezwa kwi-iron etyhidiweyo, ikharbon ikakhulu ichayima njengegrafu ye-spherical, ekhokelela ekuqinisekisweni kwentsimbi ye-ductile. Inkqubo yemveliso eqhelekileyo ye-ductile ibandakanya ukongeza inani elincinci le-magnesium ukuya kwe-iron ephantsi. Kuba i-magnesium ikhuthaza ukusekwa kwe-carbides, kufuneka yongezwe ukuba ichaze oku. Le nkqubo yonyango kwigrafu eyenza imilo ye-spherical. Ngokungafaniyo ne-Grey i-Iron, i-ductile yentsimbi ayifuniyo colonies ngexesha lenkqubo eqinisekileyo. Ngokwesiqhelo, ubungakanani be-sperhel yegrafu malunga ne-1.0% ye-colonies eyenziwe kakuhle e-Exectic kwi-Iron engwevu.
| Iipropathi zoomatshini kunye nokuhlelwa kwe-Ferric-Peritic Ductile yentsimbi | ||||||
| Ibakala lezinto ezibonakalayo | Amandla amanxuwa r / MPA Mkhulu okanye ulingana no |
Amandla anemiqathango R, o.2 / i-MPA mkhulu kune okanye ilingane ne |
I-Elongition emva kokuqhekeka ((%) Enkulu okanye ilinganayo |
I-HBW |
Ubukhulu becala / mm |
Isakhiwo esikhulu seMatrix |
| Qt350-22 | 350 | 220 | 22 | Ngaphantsi okanye ilingana no-160 | Ngaphantsi okanye ilingana no-30 | Ferrite |
| Qt400-18 | 400 | 250 | 18 | 130-175 | Ngaphantsi okanye ilingana no-30 | Ferrite |
| Qt400-15 | 400 | 250 | 15 | 135-180 | Ngaphantsi okanye ilingana no-30 | Ferrite |
| I-Qt450-10 | 450 | 310 | 10 | 160~210 | Ngaphantsi okanye ilingana no-30 | Ferrite |
| I-QTS00-7 | 500 | 320 | 7 | 170~230 | Ngaphantsi okanye ilingana no-30 | Ferrite + Pearlite |
| I-Qt550-55 | 550 | 350 | 5 | 180-250 | Ngaphantsi okanye ilingana no-30 | Ferrite + Pearlite |
| I-Qt6003 | 600 | 370 | 3 | 190-270 | Ngaphantsi okanye ilingana no-30 | I-Pearlite + Ferrite |
| I-Qt700-2 | 700 | 420 | 2 | 225-305 | Ngaphantsi okanye ilingana no-30 | I-Pearlite |
| Qt800-2 | 800 | 480 | 2 | 245-335 | Ngaphantsi okanye ilingana no-30 | I-Pearlite okanye i-sorbite |
| Qt900-2 | 900 | 600 | 2 | 280-360 | Ngaphantsi okanye ilingana no-30 | I-Marterite evuthayo okanye i-flexion I-Sterite + sorbite |